|Temperature: low temprature|
|Advantage: One time vulcanization ,without secondary vulcanization|
No new low molecules after vulcanization
Rapid vulcanization speed and low molding temperature
Excellent physical properties after formation
One time vulcanization ,without secondary vulcanization
Specification Data sheet:
Mainly used for low temperature vulcanization and silicone with odorless or thick products.
Such as: molded silicone nipple, cake pan, ashtray, sealing ring, silicone bag, PC mobile phone case or thick silicone product
Avoid to contact with nitrogen, phosphorus, sulfur and heavy metal materials,they will cause dead materials.
The cross linking agent is added by weight to Part B and should be thoroughly mixed into Part A after adding Part B,the order is important. A and B can not be mixed together.
The temperature of mixing machine which used for mixing silicone with this agent can not be higher than 45°C.Please add this agent after being cold.
Thoroughly vulcanized materials by this agent must be used up within two days.
Please choose the suitable raw materials for hot air vulcanization, bad raw materials will cause bubbles.
Platinum A and B rubbers should be placed in a space where the temperature should not exceed 25 ° C after being uniformly tempered with each other, and used within 8 hours.
To prevent cross-linking under room temperature
Method of Application:
Take 20KG as an example: TNA-65PJ: 0.6% × 20KG = 120g (A);
TNB-65PJ: 2.0% × 20KG = 400g (B). Mix 10KG Silicone Rubber and 120g TNA-65PJ first. Mark as A and let stand for about 30 minutes. Then mix 10KG Silicone rubber and 400g TNB-65PJ and mix it evenly and mark it as B, let stand for about 30 minutes. Before vulcanization molding, take equal amounts of A and B to each other to be used for extrusion vulcanization molding. (Used after cooling, the effect is best.) A, B mixed raw materials need to be placed In a space where the temperature does not exceed 250C, it should be used within 8 hours to prevent cross-linking at room temperature.
Application Ratio is Adjustable.
Product packaging: 1KG / can or 15KG / barrel